Heat Resistant Alloys
NAS800
- JISNCF800
- UNSN08800
- DIN/EN1.4876
, comparable to Incoloy® 800 Alloy
NAS800 (NCF800, UNS N08800) is a nickel-iron-chromium alloy that provides high strength and excellent resistance to oxidation and carburization at high temperatures. It also offers excellent corrosion resistance in many aqueous environments. Nippon Yakin provides this product in plate, sheet, and strip forms.
* Incoloy is a registered trademark of Special Metals Corporation.| Chemical Composition | 32Ni-20Cr-0.4Ti-0.3Al |
|---|---|
| Product shape |
 Coil Sheet Plate |
| Workability | Whether for hot working or cold working, NAS800 offers workability similar to austenitic stainless steels. For hot working, temperatures should be between 1000 and 1230℃, although light work may be done at temperatures as low as 850℃. To prevent cracks, we recommend avoiding the temperature range between 650 and 800℃. Although cold workability is similar to austenitic stainless steels, work hardening tends to be slightly lower. |
| Weldability | As with standard austenitic stainless steels, NAS800 may be welded using techniques such as TIG, MIG, and shield metal arc welding. AWS ERNiCr-3/AWS ENiCrFe-2 welding rods are often used. |
| Heat Treatment | NAS800 exhibits an austenite structure similar to austenitic stainless steels, and appropriate heat treatment procedures and requirements are similar. Typical heat treatments are as follows: ・Annealing: 980~1060℃; rapid cooling |
| Properties at High Temperatures | Because of its high nickel and chromium content, NAS800 resists oxidation and carburization at high temperatures. NAS800 is superior to Type 310S and approaches NAS600 in resistance to oxidation. Offering superior high-temperature strength nearly equal to NAS600, NAS800 is widely used in applications requiring heat resistance, as they do not become brittle due to sigma phase precipitation during use. While NAS800 is generally used at temperatures below 600℃, NAS800H/800T are recommended for applications requiring superior creep properties at higher temperatures. |
| Corrosion resistance | NAS800 offers superior corrosion resistance in oxidizing corrosive environments such as nitric acid or nitric acid-sulfuric acid. Likewise, it performs well in sodium salt and other molten salt environments, with stress corrosion cracking resistance surpassing standard austenitic stainless steels. |
| Applications | Sheathed heater, Furnace parts, Heat treatment fixtures, Heat exchangers. |